Composition of 439 Pipe and Tubing
| Grade | 439 |
|---|
| UNS Designation | S43035 |
|---|
| Nickel (Ni) |
0.50 |
| Chromium (Cr) |
17.0–19.0 |
| Iron (Fe) |
Bal. |
| Molybdenum (Mo) |
— |
| Titanium (Ti) Max. |
0.20 + 4x (C + N) Min. to 1.10 Max. |
| Aluminum (Al) Max. |
0.15 |
| Cobalt (Co) Max. |
— |
| Tungsten (W) |
— |
| Vanadium (V) Max. |
— |
| Copper (Cu) Max. |
— |
| Manganese (Mn) Max. |
1.00 |
| Niobium (Nb) plus Tantalum |
— |
| Carbon (C) Max. |
0.07 |
| Nitrogen (N) Max. |
0.04 |
| Silicon (Si) Max. |
1.00 |
| Sulphur (S) Max. |
0.030 |
| Phosphorous (P) Max. |
0.040 |
| Other Elements |
— |
Physical Properties of 439 Alloys in the Annealed Condition at -20°F to +100°F
| Â |
 |
 |
Tensile Strength | Yield Strength |
 |
 |
 |
 |
 |
 |
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 in. (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion (IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ ft2-h-°F) |
|---|
| 439 |
S43035 |
A268 |
60,000 |
415 |
60 |
30,000 |
205 |
30 |
20 |
— |
90 Rb |
29.0 |
5.6 |
168 |
439 Product Range
| Alloy | UNS Designation | Werkstoff NR. | Specifications* |
|---|
| 439 |
S43035 |
N/A |
A/SA268 |
*Note: The specifications noted including ASTM, ASME, or other applicable authorities are correct at the time of publication. Other specifications may apply for use of these materials in different applications.